Table 10. Resilient modulus test results for NH5.
NH 5-1
NH 5-2
Max.
σc
σ1
ω
γd
ω
γd
Temp
Mr
Mr
C
kg/m3 (pcf)
kg/m3 (pcf)
kPa (psi)
kPa (psi)
(%)
MPa (psi)
(%)
MPa (psi)
5.0
41 (6)
14 (2)
23
1669 (104)
0.39
59 (8518)
23.8
1664 (104)
0.4
60 (8699)
5.0
41 (6)
28 (4)
23
1669 (104)
0.40
34 (4905)
23.8
1664 (104)
0.4
36 (5257)
5.0
28 (4)
14 (2)
23
1669 (104)
0.41
45 (6473)
23.8
1664 (104)
0.4
48 (6917)
0.5
41 (6)
14 (2)
23
1669 (104)
0.42
57 (8327)
23.8
1664 (104)
0.4
73 (10,547)
0.5
41 (6)
28 (4)
23
1669 (104)
0.39
39 (5725)
23.8
1664 (104)
0.4
40 (5759)
0.5
28 (4)
14 (2)
23
1669 (104)
0.39
51 (7356)
23.8
1664 (104)
0.4
51 (7380)
0.5
41 (6)
14 (2)
23
1669 (104)
0.45
35 (5010)
23.8
1664 (104)
0.4
55 (8016)
0.5
41 (6)
28 (4)
23.8
1664 (104)
0.4
39 (5584)
0.5
28 (4)
14 (2)
23
1669 (104)
0.48
31 (4493)
23.8
1664 (104)
0.5
50 (7222)
2.0
41 (6)
14 (2)
23
1669 (104)
296 (42,874)
2.0
41 (6)
28 (4)
23
1669 (104)
185 (26,796)
2.0
41 (6)
41 (6)
23
1669 (104)
141 (20,463)
23.8
1664 (104)
231 (33,529)
2.0
28 (4)
14 (2)
23
1669 (104)
332 (48,172)
2.0
28 (4)
28 (4)
23
1669 (104)
179 (25,942)
23.8
1664 (104)
256 (37,197)
2.0
28 (4)
41 (6)
23
1669 (104)
140 (20,248)
23.8
1664 (104)
233 (33,752)
2.0
14 (2)
14 (2)
23
1669 (104)
273 (39,539)
2.0
14 (2)
28 (4)
23
1669 (104)
172 (24,924)
23.8
1664 (104)
253 (36,659)
2.0
14 (2)
41 (6)
23
1669 (104)
139 (20,193)
23.8
1664 (104)
247 (35,866)
5.0
69 (10)
138 (20)
23
1669 (104)
0.19
894 (129,651)
23.8
1664 (104)
1422 (206,262)
5.0
69 (10)
207 (30)
23
1669 (104)
0.13
927 (134,424)
23.8
1664 (104)
1329 (192,737)
10.0
69 (10)
103 (15)
23
1669 (104)
2200 (319,030)
-
10.0
69 (10)
221 (32)
23
1669 (104)
2548 (369,528)
23.8
1664 (104)
3641 (528,014)
10.0
69 (10)
338 (49)
23
1669 (104)
0.40
2770 (401,691)
23.8
1664 (104)
0.3
3378 (489,988)
10.0
69 (10)
448 (65)
23
1669 (104)
0.35
2800 (406,153)
23.8
1664 (104)
0.4
3135 (454,730)
10.0
69 (10)
558 (81)
23
1669 (104)
0.38
2980 (432,189)
23.8
1664 (104)
0.4
3054 (442,943)
10.0
69 (10)
669 (97)
23
1669 (104)
0.38
2755 (399,612)
23.8
1664 (104)
0.4
2797 (405,703)
10.0
69 (10)
896 (130)
23
1669 (104)
0.32
2516 (364,940)
23.8
1664 (104)
0.4
2411 (349,725)
20.0
69 (10)
448 (65)
23
1669 (104)
0.33
4913 (712,606)
23.8
1664 (104)
0.3
5812 (842,888)
20.0
69 (10)
669 (97)
23
1669 (104)
5261 (762,979)
23.8
1664 (104)
0.3
5506 (798,524)
20.0
69 (10)
896 (130)
23
1669 (104)
0.33
5358 (777,124)
23.8
1664 (104)
0.3
5161 (748,487)
10.0
69 (10)
221 (32)
23
1669 (104)
0.47
2851 (413,469)
23.8
1664 (104)
3663 (531,204)
10.0
69 (10)
338 (49)
23
1669 (104)
0.32
2940 (426,446)
23.8
1664 (104)
3520 (510,603)
10.0
69 (10)
448 (65)
23
1669 (104)
0.21
2934 (425,536)
23.8
1664 (104)
0.4
3391 (491,766)
10.0
69 (10)
558 (81)
23.8
1664 (104)
0.4
3248 (471,122)
10.0
69 (10)
669 (97)
23
1669 (104)
0.50
3174 (460,381)
23.8
1664 (104)
0.4
2976 (431,673)
10.0
69 (10)
896 (130)
23
1669 (104)
2925 (424,189)
23.8
1664 (104)
0.4
2690 (390,156)
5.0
69 (10)
138 (20)
23
1669 (104)
0.18
1288 (186,785)
23.8
1664 (104)
1937 (280,989)
5.0
69 (10)
207 (30)
23
1669 (104)
0.21
1302 (188,904)
23.8
1664 (104)
1816 (263,328)
2.0
41 (6)
14 (2)
23
1669 (104)
198 (28,725)
23.8
1664 (104)
104 (15,132)
2.0
41 (6)
28 (4)
23
1669 (104)
0.31
136 (19,765)
23.8
1664 (104)
72 (10,445)
2.0
41 (6)
41 (6)
23
1669 (104)
102 (14,722)
23.8
1664 (104)
55 (7970)
2.0
28 (4)
14 (2)
23
1669 (104)
0.18
139 (20,182)
23.8
1664 (104)
115 (16,610)
2.0
28 (4)
28 (4)
23
1669 (104)
99 (14,353)
23.8
1664 (104)
66 (9613)
2.0
28 (4)
41 (6)
23.8
1664 (104)
56 (8083)
2.0
14 (2)
14 (2)
23
1669 (104)
0.10
132 (19,165)
23.8
1664 (104)
117 (17,008)
2.0
14 (2)
28 (4)
23.8
1664 (104)
67 (9654)
2.0
14 (2)
41 (6)
23.8
1664 (104)
0.4
56 (8128)
0.5
41 (6)
14 (2)
23
1669 (104)
0.10
31 (4513)
23.8
1664 (104)
19 (2767)
0.5
28 (4)
14 (2)
23
1669 (104)
0.01
28 (3989)
23.8
1664 (104)
19 (2715)
0.5
14 (2)
14 (2)
23.8
1664 (104)
18 (2625)
0.5
41 (6)
14 (2)
23
1669 (104)
0.17
15 (2200)
23.8
1664 (104)
14 (2056)
0.5
28 (4)
14 (2)
23
1669 (104)
0.17
14 (2039)
23.8
1664 (104)
13 (1945)
5.0
41 (6)
14 (2)
23
1669 (104)
0.29
16 (2328)
23.8
1664 (104)
0.4
12 (1793)
5.0
28 (4)
14 (2)
23
1669 (104)
0.22
15 (2140)
23.8
1664 (104)
0.4
12 (1701)
13