Table A2 (cont'd).
Exposure
time
Analyte
(hr)
NB
TDCE
MNT
TCE
CLB
ODCB
PDCB
PCE
XLPE
8.47e
3.42j
4.80f
2.24k
1.34i
0.609i,j
0.414j
0.552i
1
6.00e
1.70i
2.42g,h
0.910j,k
0.498h
0.177g
0.106i,j
0.160h
8
4.53g
0.928k
1.60i,j
0.508l
0.292k
0.108i,j,k
0.065j
0.090i
24
3.65f
0.584j
1.19i
0.327i
0.198i,j
0.076i
0.048f
0.059g,h
48
2.95f
0.390i
0.906i
0.235j
0.117i,j
0.056h
0.035j
0.041g
72
PE lining in an EVA shell
8.37e,f
3.11j,k
4.91e,f
2.16k
1.34i
0.683i
0.479j
0.610i
1
5.54f
0.832j
2.16h,i,j
0.557j,k,l
0.337h
0.139g
0.087i,j
0.107h
8
3.38i
0.340l
1.01l
0.221m
0.138l
0.062j,k
0.030j
0.054i
24
1.74i
0.177k
0.421j
0.110i
0.067j
0.035i
0.021f
0.038g,h
48
0.900i
0.090j,k
0.209l
0.070j
0.043j
0.022h
0.016j
0.026g
72
PE cross-linked to EVA shell
7.98f
2.95k
4.49f
2.07k
1.27i
0.607i,j
0.414j
0.554i
1
5.14f,g
0.786j,k
1.95i,j
0.528j,k,l
0.322h
0.142g
0.073i,j
0.133h
8
2.76j
0.327l
0.765m
0.196m
0.119l
0.055j,k
0.029j
0.051i
24
1.42j
0.183k
0.336j,k
0.109i
0.065j
0.027i
0.016f
0.031h
48
0.764i
0.102i,j,k
0.186l,m
0.072j
0.043j
0.019h
0.014j
0.023g
72
P(VDF-HFP)
8.03f
7.30f
4.76f
8.36g
5.31f
3.08f
2.51f
3.79f
1
5.31f,g
5.37f
2.28g,h,i
5.27f
2.73e
1.25f
1.00g
1.83e,f
8
3.96h
3.73g
1.48j
3.37h
1.77h
0.785g
0.614h
1.04f,g
24
3.09g
2.90f
1.07i
2.48f
1.27h
0.546g
0.426f
0.758d,e,f
48
2.32g
1.98f
0.778j,k
1.68g
0.889h
0.374g
0.285h
0.495e,
72
Fluoroelastomer
7.08g
6.73g,h
3.88g
7.23h
4.31g
2.42g
1.99g
2.95g
1
4.65h
5.00f
1.89j
4.51g
2.26e,f
1.04f
0.824g
1.45f
8
3.33i
3.21h
1.24k
2.78i
1.42i
0.641h
0.512h,i
0.790g
24
2.73h
2.46g
0.968i
2.08f
1.05h
0.478g,h
0.377f
0.580e,f,g
48
2.09g,h
1.70f
0.714k
1.41g
0.754h
0.331g
0.259h,i
0.390e,f
72
Polyamide*
7.99f
6.34h,i
5.30e
5.10j
3.14h
1.34h
1.02i
2.23h
1
4.99g,h
3.11h
2.29g,h,i
2.09i
1.11g
0.301g
0.247i
0.666g
8
3.27i
1.83j
1.31k
1.21k
0.744j
0.186i
0.155j
0.374h
24
2.50h
1.38i
0.990i
0.881h
0.517i
0.141h,i
0.118f
0.278f,g,h
48
1.95h
0.832h
0.747k
0.633i
0.275i
0.105h
0.087i,j
0.202f,g
72
PP
10.84c
6.07i
9.17c
5.81i
4.33g
2.39g
1.53h
1.73h
1
9.70c
3.90g
7.13e
3.03h
2.08f
0.944f
0.566h
0.665g
8
9.05e
2.60i
6.00g
1.90j
1.36i
0.615h
0.356i
0.388h
24
8.45d
1.81h
5.16g
1.30g
0.972h
0.458g,h
0.263f
0.283e,f,g,h
48
7.62d
1.40g
4.21g
1.00h
0.727h
0.338g
0.192h,i,j
0.211f,g
72
ETFE*
11.1b,c
6.83g
10.3b
9.71f
8.43e
7.56e
5.38e
5.93d
1
9.96c
4.84f
8.62d
6.74e
5.76d
4.75e
2.86f
3.37d
8
9.24e
3.11h
7.42f
4.22g
3.88g
3.04f
1.56g
1.73e
24
8.56d
2.37g
6.44f
3.14e
2.88g
2.21f
1.09e
1.26d
48
7.64d
1.82f
5.32f
2.33f
2.13g
1.56f
0.737g
0.871d
72
PTFE*
11.6a
8.31e
11.2a
10.6e
9.62d
8.46d
6.15d
5.18e
1
10.7b
6.15e
9.69c
6.67e
6.14d
4.95e
3.04f
2.05e
8
10.6d
4.57f
9.77e
4.78f
5.21f
3.79e
2.01f
1.25f
24
10.5c
3.33e
9.30e
3.33e
3.91f
2.77e
1.38e
0.827d,e
48
10.3c
2.74e
8.90e
2.68e
3.21f
2.23e
1.09f
0.665d,e
72
For each analyte and sampling time, values with the letter "a" are not significantly different from the
controls. For values marked with letters other than "a," all values marked with the same letter are not
significantly different from each other.
* Tubing had a different material surface-area-to-solution-volume ratio than other tubings.
23
Previous Page